GENERAL FEATURES

• It is a one-component, based on water and modified polyurethane resins, colored, thixotropic paint that once dry forms an elastic, continuous layer, fully adhered to the substrate, without joints or overlaps, elastic, pigmented, aliphatic (resistant to UV rays). To be used on concrete, mortar, cement, ceramics, metal, wood.
• Its consumption depends on the situation of the support, irregularities it presents or level of planimetry.
• It must be applied in sound and resistant substrates, with no presence of humidity/water on the surface whether at the time of application or subsequently (pressure from phreatic water level, damp-water).
• The application must be carried out on firm and dry substrates, at a substrate temperature 3ºC higher than the dew point, with an ambient temperature higher than 8 ºC and an R.H. less than 80%.

YIELD

The recommended consumption is approximately 1.5 to 2 kg/sqm (0.92 mm) applied in one or several layers, depending on the type of application and nature of the substrates.

PACKAGING

Metal tins in three formats: 6 kg and 25 kg.

STORAGE AND SHELF LIFE

12-months shelf life is stored in original containers in a dry environment at a temperature between 5-35 ºC (41-95°F). Keep away from direct sunlight, extreme heat, cold or moisture. Once the tin has been opened, the product must be used

APPLICATION METHOD

Cement or concrete substrates:  Concrete should be completely cured (concrete curing takes 28 days) or, in any case, the maximum level of humidity allowed for the substrate should be verified, depending on the primer used. Concrete must be strong, cohesive and dry, having a correct planimetry, high surface resistance, eliminating laitance, graise, oils or release agents, without excessive irregularities. In some cases i s necessary to perform physical processes (substrate preparation (sanding, polishing, shot blasting or milling)) to remove surface slurry, release agents, as well as to open the surface pore and achieve an adequate anchoring profile.Existing holes or areas with a lack of material must be repaired using some of our epoxy resins: Primer EP-1020/Primer EP-1010. Mastic PU must be used on fissures or small cracks on the surface. In joints (width < 15 mm): remove old material, clean and fill with Mastic PU. In joints (width >15 mm): remove old material, clean and fill with Mastic PU. Complement with a Tecnoband 100 band on the upper part. In structural/expansion joints: remove old material, clean and fill with Mastic PU. General cleaning of the substrate. PRIMING: use Primer PU-1050/Primer PUc-1050, Primer EP-1020, Primer EP-1010 or Primer WET, depending on the existing moisture in the substrate. Apply two coats impregnating a fiberglass reinforcement and allowing it to dry. (approximate consumption per coat of 0.750 kg/sqm). The final consumption should be approx. 2 kg/sqm. In the case of a very porous substrates, apply a first layer diluted with water (15%), to increase adhesion.

NOTE: For other types of substrates, weather conditions or the substrate to be applied, consult our technical department.

HEALTH AND SAFETY

Respiratory Protection: When handling or spraying use an air-purifying respirator. Skin protection: Use rubber gloves, remove immediately after contamination. Wear clean body-covering. Wash thoroughly with soap and water after work and before eating, drinking, or smoking. Eye / Face: Wear safety goggles to prevent splashing and exposure to particles in the air. Waste: Waste generation should be avoided or minimized. Incinerate under controlled conditions in accordance with local laws and national regulations. Re-occupancy of the work site without respiratory equipment is minimum 24 hours providing the correct ventilation for the area sprayed. Contractors and applicators must comply with all applicable and appropriate guidelines for storage and safety guidelines.These safety recommendations for handling, are necessary for the implementation process as well as in the pre and post, on exposure to the loading machinery.  Dispose waste in accordance with star or/and local regulations.

TECHNICAL AND CHEMICAL PROPERTIES

Results were performed in the laboratory at 23ºC (73ºF) and 50% RH, under controllable conditions. These values may vary depending on the application, climatology, or substrate conditions.